Placa de desgaste de aço da placa de aço de sobreposição bimetal Hardfacing
obtenha o ultimo preçoTipo de pagamento: | T/T,L/C,D/P |
Incoterm: | FOB,CFR,CIF,EXW |
transporte: | Ocean,Express,Land |
porta: | Qingdao,Tianjin,Shanghai |
SHANDONG HUITONG STEEL CO.,LTD
Tipo de Negócio:Empresa de comércio , Fabricante
principais Mercados: África , Ásia , leste Europeu , Europa , No mundo todo
Exportador:51% - 60%
certs:ISO9001, API, ASME, CE
Descrição:Placa de aço de sobreposição bimetal,Placa de cromo hardfacing,Placa de aço bimetal vestida
Tipo de pagamento: | T/T,L/C,D/P |
Incoterm: | FOB,CFR,CIF,EXW |
transporte: | Ocean,Express,Land |
porta: | Qingdao,Tianjin,Shanghai |
marca: H-Tong
Standard: Aisi, Astm, Din, Gb
Place Of Origin: China
Species: Steel Plate
Production Process: Hot Rolled
Application: Boiler Plate, Container Plate, Ship Plate
Special Steel: Wear Resistant Steel, High-Strength Steel Plate
Tolerance: ±1%, ±3%
Category: Cold Rolled Steel Sheet, Boiler Vessel Plate, Low-Alloy Plate, Hot Rolled Steel Sheet, Steel Plate, Ship Steel Plate
Processing Service: Welding, Cutting, Decoiling, Punching, Bending
Surface Treatment: Coated, Clean, blasting and painting according to customer requirement
Thickness: 3-120mm
Width: 600-1500mm, 1800-2000mm,2500-3500mm
Length: 2000-3000mm, 6000-12000mm
Unidades de venda | : | Ton |
Tipo de pacote | : | pacote com tira de aço |
Exemplo de imagem | : |
Placa de desgaste de sobreposição de carboneto cromado são fabricados soldando uma ou várias camadas resistentes ao desgaste em uma placa de base de aço de carbono médio ou baixo.
A liga de sobreposição possui uma grande quantidade de partículas duras de carboneto de cromo, o que faz com que a placa tenha um bom desgaste e resistência ao impacto.
Faixa de espessura de sobreposição : 3-25mm
Tamanho da placa de desgaste: 1500*3000, 1400*3000.1400*3400, 1400*3500, 2100*3500, personalizado.
Placa de aço de sobreposição de carboneto cromo é usada para fazer muitas peças de desgaste complexas para serem posicionadas em locais de alto desgaste.
Podemos fornecer corte de placas, flexão, aparafusamento, socos e soldagem de acordo com os desenhos do cliente.
1. A placa de aço resistente a roupas é composta de placa de aço de baixo carbono e camada de resistência ao desgaste da liga. Ao trabalhar, a matriz fornece propriedades abrangentes, como força, resistência e plasticidade de resistir às forças externas, e a camada resistente à liga fornece propriedades resistentes ao desgaste que atendem aos requisitos das condições de trabalho especificadas.
2. A camada resistente a roupas de liga de aço resistente a roupas e a placa de base são a combinação metalúrgica. Por meio de equipamentos especiais e processo de soldagem automática, o fio de liga de autoproteção de alta resistência é soldado uniformemente no substrato e as camadas compostas são de uma a duas ou mais. No processo composto, devido à diferente razão de retração da liga, aparecem rachaduras transversais uniformes, o que é uma característica significativa da placa de aço resistente ao desgaste.
3.A camada resistente ao desgaste da liga é principalmente a liga de cromo, enquanto o manganês, molibdênio, nióbio, níquel e outras ligas são adicionados. A microheridade do carboneto pode atingir acima do HV1700-2000, e a dureza da superfície pode atingir o HRC58-62. A liga de carboneto tem uma forte estabilidade em alta temperatura, mantém uma alta dureza, mas também tem uma boa resistência a oxidação, dentro de 500 ℃ Uso completamente normal.
4.A camada resistente ao desgaste possui canal estreito (2,5-3,5 mm), canal largo (8-12 mm), curva (s, w), etc. É composto principalmente por liga de cromo, enquanto manganês, molibdênio, niobium, níquel , Boron e outros componentes da liga são adicionados. Com 40-60% de conteúdo de carboneto, a microheridade pode atingir acima do HV1700 e a dureza da superfície pode atingir o HRC58-62.
Product |
Wear Resistant Steel Plate |
Standard |
AISI,ASTM,DIN,JIS,GB,JIS,SUS,EN,etc. |
Thickness |
3-120mm |
Width |
600-1500mm, 1800-2000mm,2500-3500mm |
Length |
2000-3000mm, 6000-12000mm |
Grade |
NM360, NM400, NM450, NM500, AR360, AR400, AR450, AR500, AR550
QUARD400, QUARD450, QUARD500, FORA400, FORA500, RAEX400, RAEX450, RAEX500 |
Surface treatment |
Clean, blasting and painting according to customer requirement |
Technique |
Cold rolled and hot rolled |
Capacity |
10000 tons/month |
Package |
Export standard packing: wooden cases or boxes to be packed;We will pack the goods according to the factory's requirements for export. Or according to customer requirements.In addition,we will give the product good surface protection. |
Application |
metallurgy, coal, cement, power stntion, mining, building materials, petrochemical industry |
NM360 nm 400 nm 450 nm 500 Placa de aço de resistência ao desgaste
Componente químico
Steel/Grade |
C |
Si |
Mn |
P |
S |
AL |
Cr+Ni+Mo |
Nb+V+Ti |
NM360/AR360 |
0.10-0.30 |
0.20-0.40 |
1.00-2.00 |
≤0.015 |
≤0.003 |
≥0.20 |
<0.6 |
Trace Amount |
NM400/AR400 |
0.10-0.40 |
0.20-0.40 |
1.00-2.00 |
≤0.015 |
≤0.003 |
≥0.20 |
<0.9 |
|
NM450/AR450 |
0.10-0.40 |
0.20-0.40 |
1.00-2.00 |
≤0.015 |
≤0.003 |
≥0.20 |
<1.2 |
|
NM500/AR500 |
0.10-0.40 |
0.20-0.45 |
1.00-2.00 |
≤0.015 |
≤0.003 |
≥0.20 |
<1.5 |
|
NM550/AR550 |
0.10-0.50 |
0.20-0.45 |
1.00-1.50 |
≤0.015 |
≤0.003 |
≥0.20 |
<2.0 |
|
NM600/AR600 |
0.10-0.50 |
0.20-0.45 |
1.00-1.50 |
≤0.015 |
≤0.003 |
≥0.20 |
<2.5 |
Propriedades mecânicas
Material |
Tensile MPA |
Elongation% |
Impact energy -20℃ |
HBW |
NM300 |
≥1000 |
≥14 |
≥24 |
270-300 |
NM360 |
≥1100 |
≥12 |
≥24 |
330-390 |
NM400 |
≥1200 |
≥10 |
≥24 |
370-430 |
NM450 |
≥1250 |
≥7 |
≥24 |
420-480 |
NM500 |
≥1250 |
≥7 |
≥24 |
≥470 |
NM550 |
≥1250 |
≥7 |
≥24 |
≥530 |
NM600 |
≥1250 |
≥7 |
≥24 |
≥570 |
MN13 Alta placa de aço carbono de manganês
Composição química (%)
Material |
C |
Si |
Mn |
P |
S |
Mn13 |
0.90-1.20 |
0.30-0.80 |
11.0-14.0 |
≤0.035 |
≤0.30 |
Propriedades mecânicas
Tensile Strength |
Yield Point |
Elongation |
Impact Resistance |
Initial Hardness (HB) |
Hardness after Hardened (HB) |
180° old Bending Test |
≥900MPa |
≥295 |
≥40% |
ak≥90J |
200-250 |
≥300 |
Qualified |
Podemos produzir tamanhos, espessuras, larguras e materiais diferentes de acordo com seus requisitos
1) Técnica de fabricação
Cortar grandes placas de aço como suas necessidades para tornar a superfície da placa brilhante, movendo e moendo, também pode fazer orifícios e fazer graus de ângulo e pode soldar pelo desenho.
Para a espessura abaixo de 30 mm, corte por laser; Para espessura acima de 30 mm, principalmente o corte de chama oxi.
Para a espessura da placa de aço de 200 mm, porque durante o corte da chama, a temperatura é muito alta; portanto, a placa de aço de partes de corte pode ser quebrada na parte do ângulo, nossos trabalhadores repararão os ângulos para serem boas condições.
2 ) Aplicação
A placa de aço resistente ao desgaste com alta resistência ao desgaste e bom desempenho de impacto é bom, pode ser cortado, flexão, soldagem etc., pode adotar soldagem, soldagem de plugue, conexão de parafuso de conexão com outras estruturas, como a cena da manutenção O processo possui as características de economia de tempo, conveniente e amplamente utilizado em metalurgia, carvão, cimento, central de energia, vidro, mineração, materiais de construção, tijolo e indústria petroquímica, em comparação com outros materiais, tem um desempenho de alto custo, foi favorecido por mais e mais compradores.
Sobre nós
Entre em contato conosco
Copyright © 2024 SHANDONG HUITONG STEEL CO.,LTDTodos os direitos reservados.
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.